<div class="csl-bib-body">
<div class="csl-entry">Singewald, T. D., Bruckner, T., Gruber, R., Schimo-Aichhorn, G., Hader-Kregl, L., Poeller, S., Mueller, M., Kern, C., Luckeneder, G., Stellnberger, K.-H., Strauß, B., Hafner, M., & Valtiner, M. (2022). Water-uptake in hollow glass microspheres and their influence on cathodic and anodic delamination along the polymer/metal-interface. <i>Corrosion Science</i>, <i>196</i>, Article 110045. https://doi.org/10.1016/j.corsci.2021.110045</div>
</div>
-
dc.identifier.issn
0010-938X
-
dc.identifier.uri
http://hdl.handle.net/20.500.12708/142066
-
dc.description.abstract
Water-uptake in hollow glass microspheres (HGM) filled polymers, and in turn corrosion processes along the polymer/metal-interface are not well studied to date. Here, we examine water absorption and diffusion of two epoxy adhesives in the absence and presence of HGM on zinc coated steel using electrochemical impedance spectroscopy and height-regulated scanning Kelvin probe. Mild filiform corrosion was detected on all epoxy adhesive coated Zn-Al-Mg (ZM) surfaces during Cataplasma aging, suggesting anodic delamination as degradation mechanism. In contrast substantial cathodic delamination and blistering was observed for epoxy/electrogalvanized steel samples (ZE). Hence, HGM containing coatings can inverse effects on ZM or ZE coated steel, having important implications for industrial application.
en
dc.language.iso
en
-
dc.publisher
PERGAMON-ELSEVIER SCIENCE LTD
-
dc.relation.ispartof
Corrosion Science
-
dc.subject
Epoxy coating
en
dc.subject
EIS
en
dc.subject
Scanning Kelvin Probe
en
dc.subject
Interface
en
dc.subject
Interfacial delamination
en
dc.subject
Water uptake
en
dc.title
Water-uptake in hollow glass microspheres and their influence on cathodic and anodic delamination along the polymer/metal-interface