<div class="csl-entry">Doblhoff-Dier, V. (2008). <i>Corrosion pits and influence of environment on fatigue crack growth in steam turbine steel</i> [Diploma Thesis, Technische Universität Wien]. reposiTUm. http://hdl.handle.net/20.500.12708/183780</div>
</div>
-
dc.identifier.uri
http://hdl.handle.net/20.500.12708/183780
-
dc.description.abstract
The present diploma thesis deals with corrosion pitting and crack growth in martensitic stainless steel of a kind widely used in turbine blades. Corrosion and crack prediction contribute to increased safety and reliability in power plants and minimize the costs of forced outage, repair and inspection. Experiments concerning the pitting and the crack propagation were conducted in the course of this thesis.<br />
de
dc.description.abstract
Die vorliegende Diplomarbeit beschäftigt sich mit Lochfraßkorrosion und Rissausbreitung in martensitischem rostreien Stahl. Vorhersagen der Korrosion und Rissausbreitung tragen zu erhöhter Sicherheit in Kraftwerken bei und minimieren Kosten von Ausfällen, Instandsetzung und Inspektion.<br />Im Rahmen dieser Diplomarbeit wurden Experimente zu dieser Thematik durchgeführt.
en
dc.language
English
-
dc.language.iso
en
-
dc.subject
Lochfraßkorrosion
de
dc.subject
Ermüdungsrissausbreitung
de
dc.subject
Korrosionsermüdung
de
dc.subject
Bruchflächen-Fraktographie
de
dc.subject
zyklische Spannungsintensität
de
dc.subject
hohe Lastwechselzahlen
de
dc.subject
Corrosion pits
en
dc.subject
fatigue crack growth
en
dc.subject
corrosion fatigue
en
dc.subject
fractography - fracture surfaces
en
dc.subject
cyclic stress intensity
en
dc.subject
very high cycle fatigue
en
dc.title
Corrosion pits and influence of environment on fatigue crack growth in steam turbine steel