Hybrid Alloyed Sinter Hardening Steels Based on Different Prealloyed Powders

Abstract

Sinter hardening grade steels were prepared using hybrid alloying by combining Cr-Mo and Mo prealloyed powders with fine Mn-Si masteralloy powders. Compacts from both base powders showed the “internal getter” effect, which however was much more pronounced for the Cr-Mo powders because of the markedly high starting oxygen content. Combining the base powders with the masteralloy resulted in the desired sinter hardenability, the Mo prealloyed powder resulting in somewhat better properties because of more complete dissolution of the masteralloy and lower residual oxygen content.

Sinterhärtende Stähle wurden durch Hybridlegierungstechnik hergestellt, indem Cr-Mo- bzw. Mo-vorlegierte Basispulver mit feinen Mn-Si-Masteralloy-Pulvern kombiniert wurden. Presslinge aus beiden Basispulvern zeigten den Effekt des „internal gettering“, der aber im Fall des Cr-Mo-Pulvers wegen des markant höheren Ausgangsgehalts an Sauerstoff sehr viel stärker war. Die Kombination der Basispulver mit der Masteralloy resultierte in erwünschtem, sinterhärtendem Verhalten, wobei das Mo-Basispulver aufgrund vollständigerer Auflösung der Masteralloy-Partikel beim Sintern und geringeren Restsauerstoffgehalts etwas bessere Eigenschaften ergab.