Title: Influence of non-superconducting additions on the pinning behavior in MgB2 wires and bulk samples : a comparative study
Language: English
Authors: Mohammad, Saleh 
Qualification level: Doctoral
Advisor: Reissner, Michael
Assisting Advisor: Mohn, Peter
Issue Date: 2008
Citation: 
Mohammad, S. (2008). Influence of non-superconducting additions on the pinning behavior in MgB2 wires and bulk samples : a comparative study [Dissertation]. reposiTUm. https://resolver.obvsg.at/urn:nbn:at:at-ubtuw:1-22682
Number of Pages: 100
Qualification level: Doctoral
Abstract: 
Ziel dieser Arbeit war das Studium des Einflusses verschiedener Substitutionen auf das Pinningverhalten von MgB2 Drähten mittels Untersuchung der kritischen Stromdichten und magnetischer Relaxationen.
Drähte mit unterschiedlicher Konzentration von SiC Beimengungen, sowie mit gleicher Konzentration aber unterschiedlichen Verbindungen (SiC, B4C, Al2O3) wurden in einem Vibrationsmagnetometer gemessen. Die Ergebnisse werden mit jenen von Bulk-Proben verglichen, welche ohne und mit Substitution von Al und SiC hergestellt wurden, um den Einfluss des Herstellungsprozesses zu erfassen.
Die Feld- und Temperaturabhängigkeit der kritischen Stromstärke wurde mittels verschiedener Pinning Modelle analysiert. Aus der Zeitabhängigkeit des magnetischen Momentes wurden die mittlere effektive Aktivierungsenergie, Aktivierungsenergieverteilungen sowie der Zusammenhang zwischen Aktivierungsenergie und Stromdichte bestimmt und im Modell kollektiven Pinnings interpretiert.
Die Analyse der Pinningkraft weist stark auf Korngrenzen - Pinning als Hauptmechanismus hin. Aus der Temperaturabhängigkeit der kritischen Stromdichte wurde auf delta-l Pinning als wahrscheinlichstem Prozess geschlossen.
Die Analyse der Relasationsmessungen deutet ebenfalls auf 2D - Pinning hin.

The aim of this work was to study the influence of different additions on flux pinning behavior of MgB2 wires by investigation of the critical current density and magnetic relaxation. Wires with different concentration of SiC and with same concentration but different additives (SiC, B4C, Al2O3) were measured in a vibrating sample magnetometer. The results are compared with those obtained from bulk samples prepared without and with substitution of Al and SiC to study the effect of preparation process. The field and temperature dependence of the critical current density is analyzed in terms of different pinning models. From the time dependence of the magnetic moment, the mean effective activation energy, activation energy distributions and the current-energy relation were determined and interpreted in terms of collective pinning theory.
The analysis of pinning force strongly supports the grain boundary pinning as the main mechanism. From the temperature dependence of critical current density it is concluded that delta-l core pinning is most probable. The analysis of the relaxation measurements also favors 2D pinning.
Keywords: MgB2; Supraleiter; Relaxation; kritische Stromdichte
MgB2; Superconductor; Relaxation; Critical current density
URI: https://resolver.obvsg.at/urn:nbn:at:at-ubtuw:1-22682
http://hdl.handle.net/20.500.12708/14383
Library ID: AC05036903
Organisation: E138 - Institut für Festkörperphysik 
Publication Type: Thesis
Hochschulschrift
Appears in Collections:Thesis

Files in this item:


Page view(s)

9
checked on Feb 18, 2021

Download(s)

40
checked on Feb 18, 2021

Google ScholarTM

Check


Items in reposiTUm are protected by copyright, with all rights reserved, unless otherwise indicated.