Doblhoff-Dier, V. (2008). Corrosion pits and influence of environment on fatigue crack growth in steam turbine steel [Diploma Thesis, Technische Universität Wien]. reposiTUm. http://hdl.handle.net/20.500.12708/183780
Lochfraßkorrosion; Ermüdungsrissausbreitung; Korrosionsermüdung; Bruchflächen-Fraktographie; zyklische Spannungsintensität; hohe Lastwechselzahlen
de
Corrosion pits; fatigue crack growth; corrosion fatigue; fractography - fracture surfaces; cyclic stress intensity; very high cycle fatigue
en
Abstract:
The present diploma thesis deals with corrosion pitting and crack growth in martensitic stainless steel of a kind widely used in turbine blades. Corrosion and crack prediction contribute to increased safety and reliability in power plants and minimize the costs of forced outage, repair and inspection. Experiments concerning the pitting and the crack propagation were conducted in the course of this thesis.<br />
de
Die vorliegende Diplomarbeit beschäftigt sich mit Lochfraßkorrosion und Rissausbreitung in martensitischem rostreien Stahl. Vorhersagen der Korrosion und Rissausbreitung tragen zu erhöhter Sicherheit in Kraftwerken bei und minimieren Kosten von Ausfällen, Instandsetzung und Inspektion.<br />Im Rahmen dieser Diplomarbeit wurden Experimente zu dieser Thematik durchgeführt.