Processing of Steelmaking Slags into Artificial Granular Aggregate for Concrete by Forced Carbonation

Abstract

This article presents the results of experimental studies to determine the possibility of processing steelmaking slags into an artificial granulated filler for concrete by the method of forced carbonization and the stabilization of the obtained filler in the concrete matrix over time. The utilization of metallurgical waste and technogenic CO₂ is a global problem. In this work, the method of the granulation of finely ground converter (BOF) and electric steelmaking (EAF) slags was used to obtain artificial granules and their subsequent forced carbonization in the developed laboratory carbonization chamber. Within the framework of this study, the quantitative binding of CO₂ by granules based on BOF and EAF slags was established, which amounted to 5.2 and 7.8% by weight, respectively. It was determined that the mass loss during crushability testing, indirectly characterizing the actual compressive strength of the granule material, depending on the type of slag and grain size, ranges from 13.6 to 42.3%, which is quite sufficient for using this artificial filler in concrete production. Based on the developed batches of fillers, concretes were obtained that have a compressive strength of 30.7 to 37.8 MPa in 28 days of hardening, which generally corresponds to concrete class B25. The preliminary studies and the results obtained indicate the prospects of processing steel slags into artificial granulated fillers by forced carbonization and using this product in concrete production.