Prediction of the Efficiency of CO2 Mineralization by Metallurgical Wastes in the Creation of Next-Generation Construction Materials Using a Chemical Thermodynamic Approach

Abstract

The article presents the results of experimental studies on the possibility of predicting the efficiency of CO2 mineralization using metallurgical wastes (MWs) from the perspective of chemical thermodynamics and on identifying, accordingly, promising MWs for the production of construction materials and products. The study examined MWs from major Russian iron and steel producers, namely: blast furnace, electric steelmaking, ferroalloy, converter steelmaking slag, as well as nepheline slag, a by-product of nepheline ore processing for alumina. The CO2 binding capacity of MWs was determined using experimental samples fabricated by semi-dry pressing of MW powders, followed by curing them in a gas atmosphere with an CO2 concentration of 80% vol. It was found that the investigated MWs are capable of absorbing and binding CO2, thereby improving their physical and mechanical properties. Experimental samples made from nepheline slag bind 11.3 to 12.0 wt.% of CO2; samples from steelmaking slags: up to 9 wt.% or more; and samples from blast furnace dump slag: approximately 5.5 wt.% At the same time, the compressive strength of samples from steelmaking slags exceeds 100 MPa, that of samples from nepheline slag approaches 80 MPa, and that of samples from blast furnace dump slag exceeds 50 MPa. It has been established that predicting the efficiency of CO2 mineralization by metallurgical wastes based solely on chemical thermodynamics is not entirely accurate. To develop a preliminary forecasting model for the carbonate hardening potential of various MWs, further studies are needed to identify additional key factors influencing the carbonate hardening process of MWs.